THÔNG SỐ MÁC THÉP DƯỚI ĐÂY CHỈ MANG TÍNH CHẤT THAM KHẢO
|
|||||||||||||||||
| Grade | Chemical Composition % | Tensile Test | |||||||||||||||
| C | Mn | P | S | Yield Strength | Tensile Strength | Elongation | |||||||||||
| ksi(N/mm2) | ksi(N/mm2) | Test piece in(mm) | % | ||||||||||||||
| Grade A | 0.17max | 0.90 max | 0.035 max | 0.035 max | 24(165) min | 45~65(310~450) | GL=8(200) | 27 min | |||||||||
| GL=2(50) | 30 min | ||||||||||||||||
| Grade B | 0.22 max | 27(185) min | 50~70(345~485) | GL=8(200) | 25 min | ||||||||||||
| GL=2(50) | 28 min | ||||||||||||||||
| Grade C | 0.28 max | 30(205) min | 55~75(380~515) | GL=8(200) | 23 min | ||||||||||||
| GL=2(50) | 27 min | ||||||||||||||||
| ASTM A537-95 Pressure Vessel Plates, Heat-treated, Carbon-Manganese-Silicon Steel | ||||||||||||||
| Grade | Thickness | Chemical Composition % | Tensile Test | |||||||||||
| Yield strength | Tensile strength | Elongation | ||||||||||||
| (t) mm | C | Si | Mn | P | S | Cu | Ni | Cr | Mo | ksi(N/mm2) | ksi(N/mm2) | Test piece | % | |
| in(mm) | min | |||||||||||||
| Class 1 | 6.00 ≦ t ≦ 38.10 | 0.24 | 0.15 ~ | 0.7 | 0.035 | 0.035 | 0.35 | 0.25 | 0.25 | 0.08 | 50(345) | 70~90 | GL=8(200) | 18 |
| min | ||||||||||||||
| max | 0.5 | ~ | max | max | max | max | max | max | (485~620) | GL=2(50) | 22 | |||
| 1.35 | ||||||||||||||
| 38.11 ≦ t ≦ 50.80 | 1 | |||||||||||||
| ~ | ||||||||||||||
| 1.6 | ||||||||||||||